• Occurrence and Crystal Structure of Zr-Ni Phases in the Zr-Mn-V-Ni Laves Phase Hydrogen Storage Electrode Alloys
  Zr-Mn-V-Ni储氢电极合金中的Zr-Ni相形成及其晶体结构研究
• The hardness and brittleness of ZrCr_2 Laves phase decrease, the fracture toughness is enhanced with the addition of alloying elements V, Nb and Mo, which implies that alloying has a softening effect on the mechanical properties of the ZrCr_2 Laves phase.
  添加合金元素V、Nb和Mo使ZrCr2Laves相化合物硬度及脆性度降低，断裂韧度显著提高，即合金化对ZrCr2Laves相起软化作用。
• The effects of the Ti/ Zr ratio and Mn/ Cr ratio on the hydrogen storage properties of Ti Mn based laves phase hydrogen storage alloys were investigated.
  研究了不同的Ti/Zr比以及Mn/Cr比对Ti-Mn基Laves相贮氢合金贮氢性能的影响；
• The results show that anti-site defects exist in the ZrCr_2 Laves phase.
  结果表明：当ZrCr2Laves相成分偏离化学计量比时，ZrCr2中存在着反位置（组分）缺陷。
• The latest progress in RE series, AB 2 type Laves phase, BCC solid solution type and Mg based hydrogen storage alloy were surveyed.
  对稀土基、AB2型Laves相、BCC固溶体型以及Mg基储氢合金的最新进展进行了简要综述；
• It is found by XRD analysis that the alloy mainly consists of C14 Laves phase with hexagonal structure and V-based solid solution phase with BCC structure. The rapid solidification leads to the decrease in content of the C14 Laves phase in the alloy.
  XRD研究表明：合金主要由六方结构的C14Laves相和体心立方结构的钒基固溶体相所组成，快速凝固减少了合金中C14Laves相的含量。
• HREM observation on long-period stacking structure of zr ( cr, v)_2 Laves phase
  Zr（Cr，V）2Laves相长周期堆垛结构的高分辨电子显微术观察
• The effects of rapid quenching on the initial activation capabilities of AB_2 Laves phase electrode alloys were investigated comprehensively. The phase structures and morphologies of as-cast and quenched alloys were determined and observed by XRD and SEM.
  研究了快淬处理对AB2型Laves相电极合金初始活化性能的影响，用XRD和SEM分析了铸态及快淬态合金的相结构，并观察了合金的微观组织形貌。
• Effect of Heat Treatment on properties of Ti-Mn based Laves Phase Hydrogen Storage Alloys
  热处理对Ti-Mn基Laves相贮氢合金性能的影响
• The main reason of rapidly quenched having a different influence on the initial activation capabilities of AB_2 Laves phase electrode alloys was the quantities of the amorphous formed by rapid quenching in alloys were different.
  快淬使AB2型电极合金活化性能发生变化的根本原因是合金中形成了不同量的非晶相。